Embossed Release Film for Prepreg

Embossed Release Film for Prepreg

Embossed Release Film for Prepreg
Embossed Release Film for PrepregEmbossed Release Film for PrepregEmbossed Release Film for PrepregEmbossed Release Film for PrepregEmbossed Release Film for Prepreg

Embossed Release Film for Prepreg

CategoriesPrepreg Release Film
BrandTAIMEI Tarpaulin Shade Fabric Manufacturer
Tensile strength Mpa≥14
Elongation at break %≥280
Copper content ppm≤20
Manganese content ppm≤10
Acetone extract %≤1.5
Update TimeDec 9,2023
Detail Information

plastic film

Poly Backer is a clear, low temperature plastic release film. With a meltpoint of 120 centigrade, it is designed for use in prepreg processing up to 120centigrade and will release from all resin system. Two type of Backer, perforated film and non-perforated film.Non-perforated film is used between tool and resin to prevent the resin stickto the tool. Perforated film can be applied in between prepreg and breatherfabric to prevent two resin from sticking. The thickness of the film is 0.16mm.

 

plastic film

Technical Indicators
Index Standard Reference
Melting Point °C >120 GB4608-84
Tensile strength Mpa ≥14 GB1040-92
Elongation at break % ≥280 GB1040-92
Copper content ppm ≤20  
Manganese content ppm ≤10  
Acetone extract % ≤1.5  
Film Specifications
Index Standard Reference
Melting Point °C >120 GB4608-84
Tensile strength Mpa ≥14 GB1040-92
Elongation at break % ≥280 GB1040-92
Copper content ppm ≤20  
Manganese content ppm ≤10  
Acetone extract % ≤1.5  
Width mm Deviation mm Thickness mm Deviation mm Weight g/m2 Deviation g/m2
1300 ±2 0.16 ±0.04 85 ±3
800 ±2 0.16 ±0.04 85 ±3
500 ±2 0.16 ±0.04 85 ±3
Index Standard Reference
Melting Point °C >120 GB4608-84
Tensile strength Mpa ≥14 GB1040-92
Elongation at break % ≥280 GB1040-92
Copper content ppm ≤20  
Manganese content ppm ≤10  
Acetone extract % ≤1.5  
Additives Primary Benefit
Anti-Static Static buildup resistance
Slip/Anti-block Agents Improved film to film slip & blocking
UV Stabilizers Resistance to effects of sunlight
Color Pigments Add color pigment concentrates to film

Note: In addition to the above specifications of products, we can also product as customer’s requirement.

 

plastic film

 

Related Products
    Review
    • Loading...
    For more detail, send us an inquiry below:
    Just Fill ln The Form Below And We Will Response To You Within 12 Hours
    *Email
    *Name
    *Tel
    *Title
    *Content
    Upload
    • Only supports .rar/.zip/.jpg/.png/.gif/.doc/.xls/.pdf, maximum 20MB.
    Sign Up to Get Latest Updates
    Contact us
    • Office: No. 6, Cuiling Road, Qingdao, Shandong, China
    • Factory: Qingdao · Weihai · Binzhou · Tai'an
    • +86-532-88915029
    • Send Email to us